A method for achieving a uniform film-type deposition on carbon fiber fabric is proposed. This method describes the preparation of carbon fiber fabrics with uniform film-type deposition for fabricating polymer composites with enhanced mechanical properties. The method provides a faster and more uniform deposition of functionalized graphene platelets on carbon fiber fabric. Additionally, the method improves the interfacial strength of carbon fiber fabrics, thereby enhancing the mechanical properties of the resulting carbon fiber reinforced polymer composites.
- Carbon fiber fabrics obtained has improved tensile and flexural properties
- Carbon fiber fabric further used in composite fabrication to improve the interfacial properties
- Carboxyl functionalized graphene (G-COOH) platelets dispersed in a solution, prepared by adding Mg (NO3)2 in DI water
- Particles are deposited as film and have no agglomerations
- Achieved uniform film-type deposition on carbon fibers fabric
Before deposition, pristine carbon fiber (CF) fabric was cut into 150mm × 150mm pieces, and copper tape was wrapped around all four edges. A dispersion solution was then prepared. The CF fabric was immersed into the suspension in the middle slot of the container and connected to the cathode (-) working electrode. Two stainless steel plates, each measuring 150mm × 150mm with a thickness of 0.6-1.4mm, were placed on either side of the working electrode and connected to the anode (+) counter electrode. The gap distance between the working electrode and the counter electrodes was set between 0.6-1.4cm. The optimized process parameters for achieving uniform particulate deposition involved applying a constant direct current voltage of 9-21V and a deposition time of 12-28 minutes.
The invention has a proof of system and is ready for deployment. Carbon fiber fabrics underwent sonication-assisted EPD with uniform film type deposition and were compared with pristine carbon fiber specimen. They showed improved tensile and flexural properties over the specimen.
9
Aerospace and defense industry, automobile industry, sports industry, marine industry, energy industry
The invention gives carbon fiber fabrics with improved tensile and flexural properties. Carbon fiber fabrics have applications in various industries such as aerospace, automobile, sports and so on. It can be used in various engineering sectors such as robotics, industrial equipment and machinery components.